Stainless' only bad deal other than galling is crevice corrosion. I have seen some bad applications where stainless sat in a de-oxygenated envorinment. it doesn't rust, it disappears...
In structiural application this can be catastrophic. That is why we see bronze rather than stainless in below-waterline applications.